$107.23

• A3 shade provides deepest A-family PLT matching
• Preloaded PLTs contain 0.2 g composite per tip
• 4 mm placement depth needs no separate capping layer
• 70 wt% and 56 vol% spherical filler loading
• 10 sec cure supports efficient deep restorations
• Quantity: 20 per Pack

Tokuyama Estelite Bulk Fill Flow PLT, A3, 0.2 g is used for direct anterior and posterior restorations that require a warmer A3 shade, deep incremental placement, and controlled preloaded-tip delivery. The A3 variant provides the deepest A-family shade in this PLT range, making it useful when surrounding tooth structure calls for greater chroma than A1 or A2.

In a Class I or Class II posterior restoration, the preloaded tip can dispense material directly into the preparation in increments up to 4 mm, helping the composite adapt closely to cavity walls before light curing. It can also support cavity lining, undercut blocking before indirect restorations, and porcelain or composite repair when A3 is the selected shade. Each pack contains 20 preloaded PLTs with 0.2 g of A3 Estelite Bulk Fill Flow composite in each tip. Dental offices ordering bulk-fill flowable composite from their supplier can buy this A3 shade, preloaded PLT format for individually portioned direct placement, distinguishing this configuration from the 3.0 g syringe version.

The light-cured restorative uses spherical filler technology with 70% filler by weight and 56% by volume, with an average filler particle size of approximately 200 nm. Controlled translucency supports light penetration through increments up to 4 mm, while the material becomes more opaque after polymerization for a natural final appearance. Its flowable consistency promotes intimate adaptation, while the filler system supports smooth polishing, gloss retention, wear resistance, flexural strength, compressive strength, and reduced polymerization shrinkage stress. Estelite Bulk Fill Flow works by maintaining higher translucency during placement so curing light can reach deeper into the restorative increment, followed by increased opacity after polymerization.

Under qualifying curing conditions, a 4 mm increment can be polymerized in approximately 10 seconds without a separate capping layer. The flowable handling helps reduce gaps and voids through close adaptation to prepared surfaces, while the cured composite provides the mechanical performance needed for posterior restorative use. This A3 PLT configuration is distinguished by its warmer shade, 0.2 g preloaded-tip delivery, 20-count presentation, 4 mm placement depth, and no-capping workflow.

These features support precise unit-dose placement, deeper A-family shade matching, efficient curing, and reliable cavity adaptation.